CK45 Steel Round Bar, CK45 Steel Round Bar Manufacturers, CK45 Steel Suppliers, CK45 Stockist, CK45 Steel Dealers, CK45 Steel Distributors, CK45 Wholesalers, CK45 Steel Traders, CK45 Steel Square Distributors, CK45 Steel Flat Bar, CK45 Steel Companies Near me.
Carbon Steel CK 45 is suitable for mean strained parts of higher dimensions (heavy forged parts) and complexed forms in vehicle manufacturing and machine engineering (e.g. ship shafts, transmission parts, wheel hubs). Lowest application temp. -25 °C, favorable creep behavior up to 480 °C.
Suitable for manufacturing various strong cutting tools with wear-resistant, resistant to impact. Advanced punching die, screw die, the toughness and complicated shape of the punch, etc. Roll cutting tool industry: scraper, serrated knife, iron knives, drill bits, etc.
Forging industry: forging die.
Screw industry: heading forming mold, such as teeth, punch.
|ASTM A681||DIN 17350||JIS G4403||GB/T 1299||ISO 4957|
Addition to other grades:
MS, EN1A, EN3B, EN8, EN8D, EN9, EN19, EN24, EN31, EN32B, EN36C, EN41B, EN43B, EN47, EN353, IS2062, 42Crmo4, HCHCR, OHNS, D2, D3, H-11, H-13, CW-1, M2, M35, M42, 2714, SKD-11, P20, P20+S, P20+Ni, SCM 420, ASTM SA-36, ASTM SA-105, SAE 1018, SAE 1020, SAE 4140, SAE 8620, 16MNCR5, 20MNCR5, C20, C35, C40, C45, C50, C60, 20C8, 40C8, 45C8, 55C8, C55MN75, SAE 52100, S40C, S355J2G3.
Our Supply Range:
People also search as:
CK45, CK45 Steel, CK45 Chemical composition, CK45 Mechanical properties, CK45 Equivalent Grades, CK45 Steel plate, CK45 Steel sheet, CK45 Manufacturers, CK45 Suppliers, CK45 Dealers, CK45 Stockist, CK45 Distributors, CK45 Wholesalers, CK45 Traders.
The following table shows the chemical composition of CK45 steel:
|Elastic modulus||217 GPa at – 100 °C|
|Elongation||4 -8 % at 20 °C|
|Poisson’s ratio||0.29 [-] at 20 °C|
|Shear modulus||75 – 80 GPa at 20 °C|
|Tensile strength||580 – 770 MPa at 20 °C|
|Yield strength||330 – 640 MPa at 20 °C|
Hardness, Rockwell C (Water quenched on 820-870°C, 5 minutes): 201~269HB
Heat Treatment of AISI 1045 (CK45) followed by furnace cooling at 50ºF (28ºC) per hour, to 1200ºF (650ºC) soaking and air cooling. Hardening of this grade is carried out from an austenitizing temperature of 1475-1550ºF (800-845ºC) and oil or water quenching.
Hardening of this grade is carried out from an austenitizing temperature of 1475-1550ºF (800-845ºC) and oil or water quenching. Flame and induction hardening may be carried out by heating quickly to the desired case depth and quenching in water or oil. This should be followed by a tempering treatment at 300-400ºF (150-200ºC) to reduce stresses in the case without affecting its hardness. A surface hardness of Rc 58 may be obtained by this treatment.
Tempering temperature / ℃ : 552
After tempering hardness HRC or higher: 201-269HB.
|Thermal expansion||10 – 10||e-6/K|
|Thermal conductivity||25 – 25||W/m.K|
|Specific heat||460 – 460||J/kg.K|
|Melting temperature||1450 – 1510||°C|
|Density||7700 – 7700||kg/m3|
|Resistivity||0.55 – 0.55||Ohm.mm2/m|
Thermal PropertiesCoefficient of thermal expansion α 1.08E-5 1/K at -100 °C
At first, Pre-Heating to 552℃，Then heat to forged temperature. Next, Soak at 820-870 °C , ensure heat thorough. Then start forged, the forged temperature no low than 560℃. After forging, cool slowly.
Full annealing of small C1045 forgings is carried out from 1450-1600ºF (790-870ºC) followed by furnace cooling at 50ºF (28ºC) per hour, to 1200ºF (650ºC) soaking and air cooling.
Density 7.8 g/cm³ at 20 °C
Machinability is good, rated at 80% that of the AISI 1112 alloy used as a 100% machining rated steel.
Ahmedabad, Amaravathi, Ambattur, Bangalore, Belgaum, Chennai, Chittoor, Coimbatore, Dindigul, Mysore, Nellore, Hyderabad, Kochi, Mangalore, Tirupur, Tuticorin, Madurai, Andhra Pradesh, Karnataka, Puducherry, Kerala, Tamil Nadu, Telangana, Salem, Thanjavur, Trichy, Erode, Vellore, Ranipet, Sivakasi, Karur, Hosur, Nagercoil, Kanchipuram, Karaikudi, Neyveli, Cuddalore, Kumbakonam, Thiruvannamalai, Pollachi, Rajapalayam, Gudiyatham, Pudukottai, Vaniyambadi, Ambur, Nagapattinam, Trivandrum, Vijayawada, Guntur, Thirupathi, Nazarathpet, Kakinada, Kurnool, Kadapa, Nizamabad, Mahabubnagar, Karimnagar.